Selective growth of single-walled carbon nanotubes and fabrication of devices on their base
Y. Kasumov et al.
IMT RAS1 and ISSP RAS2
, Chernogolovka, Russia
Equipment: SEM Zeiss EVO 50
The samples were fabricated as follows. At first, a Pt film with Cr underlayer was deposited by e-beam evaporation on oxidized
silicon wafer using photolithography mask to form contact pads and lanes. Then the wafer was cut up to obtain chips.
10 nm Al/1 nm Fe bilayer catalyst was selectively deposited by e-beam gun onto the chips using electron beam lithography and
a lift-off technique. After that the chips with deposited bilayer catalyst were heated in a furnace in air atmosphere for 2 min
in order to form Fe nanoparticles. Then the nanotubes were synthesized by single injection of acetylene CVD technique.
E-beam lithography with NanoMaker system and a lift-off process were used to pattern e-beam evaporation deposited Pd-Al electrodes contacting nanotubes.
Nanotube SQUID prototype based on 2 nanotubes.
|
Back to Image Gallery |
More images from other authors
 |
|
A. Firsov; Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, BESSY II
Reflection Zone Plates for focusing X-rays...
|
 |
|
G.Goltsman, K. Smirnov, N.Kaurova et al.; MSPU
Superconducting Hot-Electron Bolometer Mixer for Terahertz Heterodyne Receivers...
|
 |
|
J. Kouba; Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, BESSY II
Hexagonal lattice type photonic crystal in S3N4...
|
 |
|
V. Gurtovoi, A. Firsov; IMT RAS
Quantum state detector...
|
 |
|
A. Nashchekin, E. Arakcheeva, E. Tanklevskaya; Ioffe Physico-Technical Institute RAS
2D PhC with CROW based on PhC defect superlattice for slowing light...
|
 |
|
Yu. Petrov, Prof. O. Vyvenko; St. Petersburg State University
Happy New 2011 year with ion beam lithography!...
|
 |
|
A. Vystavkin, A. Kuzmin, S. Shitov, A. Kovalenko, I. Kon, A. Uvarov, et al.; Institute of Radioengineering and Electronics (IRE) of RAS
Single receiving element of superconducting terahertz hot-electron bolometer incorporated into a planar antenna...
|
 |
|
М. Knyazev, V. Starkov, D. Roshchupkin; IMT RAS
"Deep" X-ray diffraction gratings based on Si (400) crystal...
|
 |
|
E. Konstantinov, E. Demidov; Herzen State Pedagogical University
Submicron bismuth (Bi) wires...
|
 |
|
V. Gurtovoi2, V. Antonov1; Royal Holloway University1
Multiple superconducting ring ratchet...
|
|
|
|